M500026T is a Linear Low Density Polyethylene grade with narrow molecular weight distribution suitable for injection molding applications. It has been designed to give excellent flow properties with better low temperature toughness, stress crack resistance and gloss.
Processing Conditions
Typical processing conditions for M500026T are: Barrel temperature: 180 – 230°C Mold temperature: 15 -60 °C Injection pressure: 600 – 1000 Bar.
Health And Safety Considerations And Precautions
M500026T is suitable for Food contact application. Detailed information is provided in relevant Material Safety Datasheet and for additional specific information please contact SABIC local representative for certificate.
DISCLAIMER
This product is not intended for and must not be used in any pharmaceutical/medical applications.
Storage And Handling
Polyethylene resin should be stored in a manner to prevent a direct exposure to sunlight and/or heat. The storage area should also be dry and preferably do not exceed 50°C. SABIC would not give warranty to bad storage conditions which may lead to quality deterioration such as color change, bad smell and inadequate product performance. It is advisable to process PE resin within 6 months after delivery.
Typical Property Values
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| POLYMER PROPERTIES | |||
| Density | 926 | kg/m³ | 926 |
| Melt Flow Rate (MFR) | |||
| at 190℃ and 2.16 kg | 50 | g/10 min | ASTM D1238 |
| MECHANICAL PROPERTIES | |||
| Flexural Strength | 9 | MPa | ASTM D790 |
| Flexural Modulus (1% Secant) | 200 | MPa | ASTM D790 A |
| Izod Impact Strength | 500 | J/m | ASTM D256 |
| Hardness (Shore D) | 50 | - | ASTM D2240F |
| ESCR (10% Igepal), F50 | 3 | Hrs | ASTM D1693B |
| ESCR (100% Igepal), F50 | 6 | Hrs | ASTM D1693B |
| Tensile stress at yield (50mm/min) | 10 | MPa | ISO 527-2 1A |
| Tensile stress at break (5mm/min) | 12 | MPa | ISO 527-2 1A |
| Tensile strain at break (5mm/min) | >100 | % | ISO 527-2 1A |
| THERMAL PROPERTIES | |||
| Vicat Softening Point | Vicat Softening Point 88 | ℃ | ASTM D1525 |
| Brittleness Temperature | <-75 | ℃ | ASTM D746 |