PP Injection RG568MO
short description
FOB Price:
900-1100 USD/MT
Port:
Tianjin, China
MOQ:
1*40HQ
CAS No:
9003-07-0
HS Code:
3902301000
Payment:
TT, LC
description
RG568MO is a transparent polypropylene random ethylene copolymer based on proprietary Borstar Nucleation Technology (BNT) with high melt flow. This clarified product is designed for high speed injection moulding at low temperature and contains antistatic additives.
Articles produced from this product have excellent transparency, good impact strength at ambient temperatures, good organoleptic, good colour aesthetics and demoulding properties without plate-out or blooming issues.
Applications
It is widely used to Transparent containers，Hinge closures，Food storage containers， Storage boxes，Media packaging， Pumps and closure assemblies.
packaging
In 25kg bag, 28mt in one 40HQ without pallet.
Physical Properties
| NO | PROPERTY | Typical Value | TEST METHOD |
|---|---|---|---|
| 1 | Density | 900-910kg/㎡ | ISO 1183 |
| 2 | Melt Flow Rate (230℃/2.16kg) | 30g/10min | 1133 |
| 3 | Tensile Modulus (1mm/min) | 1100 MPa | ISO 527-2 |
| 4 | Tensile Strain at Yield (50mm/min) | 12% | ISO 527-2 |
| 5 | Tensile Stress at Yield (50mm/min) | 28 MPa | ISO 527-2 |
| 6 | Flexural Modulus | 1150 MPa | ISO 178 |
| 7 | Flexural Modulus(by 1% secant) | 1100 MPa | ASTM D790A |
| 8 | Charpy Impact Strength, notched (23℃) | 6kJ/㎡ | ISO 179/1eA |
| 9 | IZOD Impact Strength, notched (23℃) | 50 J/m | ASTM D256 |
| 10 | Heat Deflection Temperature(0,45MPa)** | 75℃ | ISO 75-2 |
| 11 | Vicat Softening Temperature(Method A)*** | 124,5℃ | ISO 306 |
| 12 | Haze(2mm) | 20 % | ASTM D1003 |
| 12 | Hardness, Rockwell(R-scale) | 92 | ISO 2039-2 |